PFA 美国杜邦 440HP 注塑级 热稳定 耐高温 耐腐蚀
PFA塑料为少量全氟丙基全氟乙烯基醚与聚四氟乙烯的共聚物。熔融粘结性增强,溶体粘度下降,而性能与聚四氟乙烯相比无变化。此种树脂可以直接采用普通热塑性成型加工成制品。适于制作件,减磨件、密封件、绝缘件和医疗器械零件,高温电线、电缆绝缘层,防腐设备、密封材料、泵阀衬套,和化学容器。
Chemours Teflon? PFA Grade 440 HP Extrusion and Molding Resin
Polymer,Thermoplastic,Fluoropolymer,PFA
Chemours
产品说明:
DuPont? Teflon? PFA 440 HP fluoropolymer is a special purpose resin available in clear, 2.5-mm (0.1-in.) pellets. This resin is a chemically modified form of Teflon? PFA 340 that combines many of the benefits of the parent resin with several new ones. The additional benefits may include enhanced purity, improved thermal stability while processing, and chemical inertness, for example, to ozonated fluids.
The enhanced purity of Teflon? PFA 440 HP makes it suitable for applications that require improved color, lower extractable fluorides, and freedom from other foreign materials. This product contains no additives and is designed for hostile chemical environments where purity in the parts-per-billion range is needed. Examples are in semiconductor manufacture, fluid handling systems for industry or life sciences, and instrumentation for precise measurements of fluid systems.
The improved thermal stability of Teflon? PFA 440 HP results in reduced amounts of bubbles in final parts and decreased corrosion of processing equipment. Teflon? PFA 440 HP combines the processing ease of conventional thermoplastics with properties similar to those of polytetrafluoroethylene. Properly processed products made from neat Teflon? PFA 440 HP resin provide the superior properties typical of fluoropolymer resins: retention of properties after service at 260°C (500°F), useful properties at –196°C (–320°F), and chemical inertness to nearly all industrial chemicals and solvents. Dielectric properties are excellent. Molded products have moderate stiffness and high ultimate elongation.
Three categories (A, B, and D) of Teflon? PFA 440 HP resin covering a broad range of melt flow rates (MFR) are available. The low MFR resin provides a higher degree of stress crack resistance while the high MFR resin is easier to process. In a flame situation, products of Teflon? PFA 440 HP resist ignition and do not themselves promote flame spread. When ignited by flame from other sources, their contribution of heat is very small and added at a slow rate with very little smoke.
Statements, or data, regarding behavior in a flame situation are not intended to reflect hazards presented by this or any other material when under actual fire conditions.
Applications
Applications for Teflon? PFA 440 HP include tubing; unsupported pipe or pipe linings for production of ultrapure chemicals; semiconductor component and fluid handling systems for highperformance chemical filters.
Chemours was formed from former DuPont performance chemicals businesses, including DuPont Fluoroproducts, in 2015.
Chemours Teflon? PFA Grade 440 HP Extrusion and Molding Resin 物性表
比重 | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 |
吸水率 | = 0.030 % | = 0.030 % | 24 hours; ASTM D570 |
熔体流动速率 | 14 - 19 g/10 min | 14 - 19 g/10 min | ASTM D3307 |
肖氏硬度 (邵氏 D) | 55 | 55 | ASTM D2240 |
极限抗拉强度 | 25.0 MPa | 3630 psi | ASTM D3307 |
14.0 MPa @Temperature 250 °C | 2030 psi @Temperature 482 °F | ASTM D3307 | |
抗张强度(屈服) | 13.8 MPa | 2000 psi | ASTM D3307 |
伸长率 (断裂) | 300 % | 300 % | ASTM D3307 |
480 % @Temperature 250 °C | 480 % @Temperature 482 °F | ASTM D3307 | |
弯曲模量 | 0.590 GPa | 85.6 ksi | ASTM D790 |
0.030 GPa @Temperature 250 °C | 4.4 ksi @Temperature 482 °F | ASTM D790 | |
悬壁梁缺口冲击强度 | NB | NB | ASTM D256 |
体积电阻率 | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
表面电阻率 | = 1.00e+17 ohm | = 1.00e+17 ohm | ASTM D257 |
介电常数 | 2.03 @Frequency 60.0 - 1.00e+6 Hz | 2.03 @Frequency 60.0 - 1.00e+6 Hz | ASTM D150 |
介电强度 | 80.0 kV/mm @Thickness 0.0250 mm | 2030 kV/in @Thickness 0.000984 in | Short time; ASTM D149 |
耗散因数 | 0.00010 @Frequency 60.0 - 1.00e+6 Hz | 0.00010 @Frequency 60.0 - 1.00e+6 Hz | ASTM D150 |
耐电弧性 | = 180 sec | = 180 sec | ASTM D495 |