前言：PC、PC141R、注塑级、低粘度、透明
物理性能额定值单位制测试方法比重ASTM D792--1.20g/cm3--1.19特定体积0.835cm3/gASTM D792熔流率（熔体流动速率）(300°C/1.2 kg)11g/10 minASTM D1238收缩率 - 流动(3.20 mm)0.50 到 0.70%内部方法吸水率ASTM D57024 hr0.15平衡, 23°C0.35平衡, 100°C0.58室外适用性f2UL 746C硬度额定值洛氏硬度ASTM D785M 级70R 级118机械性能额定值抗张强度3ASTM D638屈服62.1MPa断裂68.9伸长率37.0130弯曲模量4(50.0 mm 跨距)2340ASTM D790弯曲强度4(屈服, 50.0 mm 跨距)96.5ASTM D790泰伯耐磨性(1000 Cycles, 1000 g, CS-17 转轮)10.0mgASTM D1044冲击性能额定值悬壁梁缺口冲击强度(23°C)800J/mASTM D256无缺口悬臂梁冲击(23°C)3200ASTM D4812装有测量仪表的落镖冲击(23°C, Total Energy)63.8JASTM D3763落锤冲击(23°C)169ASTM D3029拉伸冲击强度5578kJ/m2ASTM D1822热性能额定值载荷下热变形温度ASTM D6480.45 MPa, 未退火, 6.40 mm138°C1.8 MPa, 未退火, 6.40 mm132维卡软化温度154ASTM D15256线形热膨胀系数 - 流动(-40 到 95°C)6.8E-5cm/cm/°CASTM E831比热1260J/kg/°CASTM C351导热系数0.27W/m/KASTM C177RTI ElecUL 746RTI ImpUL 746RTIUL 746电气性能额定值体积电阻率1.0E 17ohm·cmASTM D257介电强度(3.20 mm, in Air)15kV/mmASTM D149介电常数ASTM D15050 Hz3.1760 Hz1 MHz2.96耗散因数9.0E-40.010相比耐漏电起痕指数(CTI)PLC 2UL 746高电弧燃烧指数(HAI)PLC 1UL 746高电压电弧起痕速率 (HVTR)UL 746热丝引燃 (HWI)UL 746可燃性额定值UL 阻燃等级(0.710 mm)HBUL 94Radiant Panel Listing (UL)YES光学性能额定值折射率1.586ASTM D542透射率(2540 μm)88.0ASTM D1003雾度(2540 μm)1.0ASTM D1003注射额定值干燥温度121干燥时间3.0 到 4.0hr建议注射量40 到 60料筒后部温度271 到 293料筒中部温度282 到 304料筒前部温度293 到 316射嘴温度288 到 310加工（熔体）温度模具温度71.1 到 93.3背压0.345 到 0.689螺杆转速40 到 70rpm排气孔深度0.025 到 0.076mm备注1通过这些链接您能够访问供应商资料。我们尽量及时更新资料；不过您可以从供应商处了解资料。2UL 黄卡含有 UL 验证的易燃性和电气特性。3类型 1, 50 mm/min41.3 mm/min5Type S